拉伸强度 | 48.02MPa | 密度 | 1.22g/cm3 | 吸水率 | 0.09% |
缺口冲击强度 | 80 | 成型收缩率 | 8% |
|
产品简述
拉伸强度 | 48.02MPa | 密度 | 1.22g/cm3 | 吸水率 | 0.09% |
缺口冲击强度 | 80 | 成型收缩率 | 8% |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
物理性能 | 比重 | ASTM D-792 | 1.22 | |||
伸长率 | ASTM D-638 | >100 | % | |||
模塑收缩率 | 7-9 | |||||
吸水率 | ASTM D-570 | 0.09 | % | |||
机械性能 | 冲击强度 | 缺口 | ASTM D-256 | 80 | kg.cm/cm | |
无缺口 | ASTM D-256 | NB | kg.cm/cm | |||
拉伸强度 | ASTM D-638 | 490 | kg/cm2 | |||
弯曲强度 | ASTM D-790 | 780 | kg/cm2 | |||
弯曲模量 | ASTM D-790 | 20000 | kg/cm2 | |||
洛氏硬度 | ASTM D-785 | 110 | M(R) | |||
电气性能 | 诱电正接 | 100Hz | ASTM D-150 | 0.002 | ||
介电强度 | ASTM D-149 | 18 | KV/mm | |||
介电定数 | 100Hz | ASTM D-150 | 3.3 | |||
抗体积性 | ASTM D-257 | >1015 | Ω.cm | |||
介电定数 | 106Hz | ASTM D-150 | 3.3 | |||
热性能 | 阻燃性 | HB | ||||
线性膨胀系数 | ASTM D-696 | 9.20.000005 | mm/mm/℃ | |||
热变形温度 | 18.6kg/cm2 | ASTM D-648 | 96 | ℃ |