| 拉伸强度 | 172MPa | 密度 | 1.53g/cm3 | 弯曲强度 | 185MPa |
| 缺口冲击强度 | 127 | 成型收缩率 | 0.15% |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 比重 | ASTM D792 | 1.53 | |||
| 成型收缩率 | ASTM D955 | 0.1-0.2 | % | |||
| 机械性能 | 拉伸强度 | - | ASTM D638 | 1750 | kg/cm2 | |
| - | ASTM D638 | 172 | MPa | |||
| - | ASTM D638 | 24900 | psi | |||
| 断裂伸长率 | ASTM D638 | 3 | % | |||
| 弯曲强度 | - | ASTM D790 | 1900 | kg/cm2 | ||
| - | ASTM D790 | 185 | MPa | |||
| - | ASTM D790 | 27000 | psi | |||
| 弯曲模量 | - | ASTM D790 | 98000 | kg/cm2 | ||
| - | ASTM D790 | 9600 | MPa | |||
| - | ASTM D790 | 1395 | psi | |||
| Izod缺口冲击强度 | - | ASTM D256 | 13 | Kg.cm/cm | ||
| - | ASTM D256 | 127 | J/m | |||
| - | ASTM D256 | 2.4 | ft.ib/in | |||
| 洛氏硬度 | ASTM D785 | 121 | R | |||
| 热性能 | 热变形温度 | - | 1.82MPa | ASTM D648 | 147 | ℃ |
| - | 1.82MPa | ASTM D648 | 295 | ℉ | ||
| 阻燃性 | 1.5mm | UL94 | V-0 | |||