拉伸强度 | 142MPa | 密度 | 1.59g/cm3 | 吸水率 | 0.08% |
缺口冲击强度 | 75 | 成型收缩率 | 0.75% |
|
产品简述
拉伸强度 | 142MPa | 密度 | 1.59g/cm3 | 吸水率 | 0.08% |
缺口冲击强度 | 75 | 成型收缩率 | 0.75% |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
物理性能 | 比重 | 23℃水中24Hr | ASTM D-792 | 1.59 | ||
成形收缩率 | 23℃水中24Hr | 0.3/1.2 | % | |||
吸水率 | 23℃水中24Hr | ASTM D-570 | 0.08 | % | ||
机械性能 | 冲击强度 | 缺口 | 1/8" | ASTM D-256 | 75 | J/M |
无缺口 | 1/8" | ASTM D-256 | 640 | J/M | ||
拉伸强度 | ASTM D-638 | 142 | MPa | |||
弯曲强度 | ASTM D-790 | 205 | MPa | |||
塔伯磨耗 | CS-171kg | ASTM D-1044 | 22 | mg | ||
表面硬度 | ASTM D-785 | M90 | ||||
拉伸率 | ASTM D-638 | 3.8 | % | |||
磨擦系数 | 对钢 | ASTM D-1894 | 0.12 | |||
弯曲弹性率 | ASTM D-790 | 8.9 | GPa | |||
电气性能 | 绝缘强度 | 1mmt | ASTM D-149 | 38 | KV/mm | |
介电常数 | 60HZ | ASTM D-150 | 3.8 | |||
1KHZ | ASTM D-150 | 3.8 | ||||
耐电弧性 | ASTM D-495 | 105 | Sec | |||
介电损耗正切值 | 60HZ | ASTM D-150 | 0.043 | |||
1KHZ | ASTM D-150 | 0.022 | ||||
体积电阻 | ASTM D-257 | >10E16 | Ω.cm | |||
热性能 | 线膨胀系数 | X10-5 | ASTM D-696 | 2.5 | cm/cm | |
熔点 | 251 | ℃ | ||||
热变形温度 | 0.45MPa | ASTM D-648 | 240 | ℃ | ||
1.82MPa | ASTM D-648 | 235 | ℃ | |||
耐燃性 | UL 94 | HB |