规格级别 | 吹塑 | 加工级别 | 吹塑级 |
|
产品简述
规格级别 | 吹塑 | 加工级别 | 吹塑级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 |
密度
|
ASTM D1505 | 1.30 |
g/cm3;
|
|
机械性能 | 摩擦系数 | 与金属 - 动态 | ASTM D1894 | 0.20 | |
薄膜 |
薄膜厚度 | 经测试 | 25 |
µm
|
|
割线模量
|
MD | ASTM D882 | 1720 |
MPa
|
|
MD | ASTM D882 | 1760 |
MPa
|
||
抗张强度
|
MD: 屈服
|
ASTM D882 | 35.2 |
MPa
|
|
TD: 屈服
|
ASTM D882 | 27.6 |
MPa
|
||
MD: 断裂
|
ASTM D882 | 40.7 |
MPa
|
||
TD: 断裂
|
ASTM D882 | 41.4 |
MPa
|
||
伸长率
|
MD: 断裂
|
ASTM D882 | 440 |
%
|
|
TD: 断裂
|
ASTM D882 | 450 |
%
|
||
埃尔曼多夫抗撕强度
|
MD | ASTM D1922 | 600 |
g
|
|
TD
|
ASTM D1922 | 570 |
g
|
||
密封强调
|
ASTM F88 | 0.0093 |
N/mm
|
||
透氧率
|
ASTM D3985 | 4.9 |
cm3;·mm/m2;/atm/24 hr
|
||
水蒸气透过性
|
ASTM E96 | 47 |
g/m2;/24 hr
|
||
热性能 | 玻璃转化温度 | DSC | ASTM D3418 | 75.0 |
°C
|
熔融温度
|
ASTM D3418 | 255 |
°C
|