性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 熔体流动速率 | 372℃/5.0kg | ASTM D-1238 | 3.5 | g/10min |
物理性能 | 比重 | ASTM D-792 | 2.15 | g/cm3 | |
机械性能 | 邵氏硬度 | Shore D | ASTM D-2240 | 28 | |
拉伸模量 | 23℃ | ASTM D-638 | 550 | MPa | |
拉伸断裂强度 | 23℃ | ASTM D-638 | 26 | MPa | |
拉伸断裂伸长率 | 23℃ | ASTM D-638 | 300 | % | |
Charpy缺口冲击强度 | ASTM D-256 | No Break | |||
电气性能 | 表面电阻 | ASTM D-257 | 1.0E+17 | ohms | |
体积电阻率 | 1.0E+17 | ASTM D-257 | 1.0E+17 | ohm·cm | |
耐压 | ASTM D-149 | 38 | kV/mm | ||
介电常数 | 23℃,50Hz | ASTM D-150 | 2 | ||
介电常数 | 23℃,100000Hz | ASTM D-150 | 2 | ||
损耗因素 | 23℃,50Hz | ASTM D-150 | 0.0005 | ||
损耗因素 | 23℃,100000Hz | ASTM D-150 | 0.0005 | ||
热性能 | 熔化温度 | 280-290 | ℃ | ||
峰值晶化温度 | ASTM D-3418 | 255-265 | ℃ | ||
线型热膨胀系数-Flow | ASTM D-696 | 0.00016 | cm/cm/℃ | ||
比热 | 23℃ | ASTM C-351 | 1000 | J/kg/℃ | |
导热 | ASTM C-177 | 0.2 | W/m/K | ||
其它性能 | 阻燃等级 | UL 94 | V-0 | ||
氧指数 | ASTM D-2863 | 95 | % |