断裂伸长率 | 3 | 拉伸强度 | 147 | 密度 | 1.72 |
缺口冲击强度 | 120 | 成型收缩率 | 0.5 | 加工级别 | 注塑级 |
|
产品简述
断裂伸长率 | 3 | 拉伸强度 | 147 | 密度 | 1.72 |
缺口冲击强度 | 120 | 成型收缩率 | 0.5 | 加工级别 | 注塑级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
基本性能 | 吸水率 | ASTM D-570 | 0.22 | % | ||
物理性能 | 摩檫系数 | 动 | ASTM D-1894 | 0.16 | ||
静 | ASTM D-1894 | 0.12 | ||||
Taber 磨耗量 | ASTM D-1044 | 14 | mg/1000 cycles | |||
比重 | ASTM D-792 | 1.41 | ||||
模缩系数 | 18~21 | cm/cm×103 | ||||
机械性能 | 弯曲模量 | ASTM D-790 | 26500 | kg/cm2 | ||
伸长率 | ASTM D-638 | 45 | % | |||
缩性热伸张系数 | ASTM D-695 | 10×10-5 | cm/cm/℃ | |||
弯曲强度 | ASTM D-790 | 1000 | kg/cm2 | |||
张力 | ASTM D-638 | 625 | kg/cm2 | |||
洛氏硬度 | ASTM D-785 | 82 | M(R) | |||
冲击强度 | 无缺口 | ASTM D-256 | 70.0 | kg.cm/cm | ||
缺口 | ASTM D-256 | 6.0 | kg.cm/cm | |||
电气性能 | 诱电正接 | ASTM D-150 | 0.007 | |||
抗体积性 | ASTM D-257 | 1×1014 | Ω.cm | |||
介电系数 | ASTM D-149 | 24 | KV/MM | |||
介电定数 | ASTM D-150 | 3.8 | ||||
抗弧性 | ASTM D-495 | 240 | sec | |||
抗表面性 | ASTM D-257 | 1×1016 | Ω | |||
热性能 | 热变形温度 | 4.6kg/cm2 | ASTM D-648 | 160 | ℃ | |
热变形温度 | 18.6kg/cm2 | ASTM D-648 | 110 | ℃ | ||
燃烧性 | 1/32" | HB |