| 拉伸强度 | 380MPa | 密度 | 0.903g/cm3 | 熔体流动速率 | 11g/10min |
| 缺口冲击强度 | 2.5 | 成型收缩率 | 1.7% |
在线订购说明
保障消费者权益，真正做到正品交易，杜绝假冒伪劣产品
021-58958519 13061808058(蒋先生) 13424755533(赵先生)
联系上海松翰
| 021-58958519 | |
| 13061808058(蒋先生) | |
| 13424755533(赵先生) | |
| |
|
|
产品简述
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-792 | 0.903 | g/cm3 | |
| 熔体流动速率 | ASTM D-1238 | 11.0 | g/10min | ||
| 物理性能 | 雾度 | ASTM D-1003 | <2 | % | |
| 机械性能 | Young's Modulus | ASTM D-882 | 9 | Mpa | |
| 断裂伸长率 | ASTM D-638 | >500 | % | ||
| IZOD冲击强度 | ASTM D-256 | 2.5 | kg.cm/cm | ||
| 弯曲模量 | ASTM D-790A | 16 | Mpa | ||
| 摩擦系数 | ASTM D-1894 | 0.5 | - | ||
| 抗张强度（屈服） | ASTM D-638 | 380 | Mpa | ||
| 洛氏硬度 | ASTM D-785 | 105 | R scale | ||
| Mold Shinkage (MD/TD) | ASTM D-955 | 1.5-1.9 | % | ||
| 延伸率（屈服） | ASTM D-638 | 10 | % | ||
| 热性能 | 维卡软化点 | ASTM D-1525B | 152 | ℃ | |
| 热变形温度 | ASTM D-648 | 125 | ℃ | ||
| Heat Sealing Temp | LG-Caltex | 150 | ℃ | ||