拉伸强度 | 380MPa | 密度 | 0.903g/cm3 | 熔体流动速率 | 11g/10min |
缺口冲击强度 | 2.5 | 成型收缩率 | 1.7% | 加工级别 | 注塑级 |
特性级别 | 阻燃级 |
|
产品简述
拉伸强度 | 380MPa | 密度 | 0.903g/cm3 | 熔体流动速率 | 11g/10min |
缺口冲击强度 | 2.5 | 成型收缩率 | 1.7% | 加工级别 | 注塑级 |
特性级别 | 阻燃级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 密度 | ASTM D-792 | 0.903 | g/cm3 | |
熔体流动速率 | ASTM D-1238 | 11.0 | g/10min | ||
物理性能 | 摩擦系数 | ASTM D-1894 | 0.7 | - | |
雾度 | ASTM D-1003 | 0.5 | % | ||
机械性能 | 抗张强度(屈服) | ASTM D-638 | 380 | Mpa | |
延伸率(屈服) | ASTM D-638 | 10 | % | ||
Mold Shinkage (MD/TD) | ASTM D-955 | 1.5-1.9 | % | ||
弯曲模量 | ASTM D-790A | 16 | Mpa | ||
洛氏硬度 | ASTM D-785 | 105 | R scale | ||
断裂伸长率 | ASTM D-638 | >500 | % | ||
IZOD冲击强度 | ASTM D-256 | 2.5 | kg.cm/cm | ||
热性能 | 维卡软化点 | ASTM D-1525B | 152 | ℃ | |
热变形温度 | ASTM D-648 | 124 | ℃ | ||
Heat Sealing Temp | LG-Caltex | 150 | ℃ | ||
其它性能 | Young's Modulus | ASTM D-882 | 8.9 | Mpa |