备注:石墨纤维增强。
详细数据
订购指南
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D1457 | 2.11 | g/cm3 | |
| 硬度计硬度 | 支撑D | ASTM D2240 | 55 | ||
| 机械性能 | 屈服抗张强度 | ASTM D1457 | 17.9 | MPa | |
| 屈服伸长率 | ASTM D1457 | 230 | % | ||
| 压缩强度 | 25%应变 | ASTM D695 | 23.4 | MPa | |
| 剪切强度 | 27℃ | ASTM D732 | 19.3 | MPa | |
| 38℃ | ASTM D732 | 18.6 | MPa | ||
| 66℃ | ASTM D732 | 16.5 | MPa | ||
| 93℃ | ASTM D732 | 15.5 | MPa | ||
| 149℃ | ASTM D732 | 14.5 | MPa | ||
| 摩擦系数 | 与自身-动态 | ASTM D1894 | 0.070 | ||
| 与自身-静态 | ASTM D1894 | 0.050 | |||
| 负载变形 | 26℃,14MPa | ASTM D621 | 8.00 | % | |
| 149℃,6.9MPa | ASTM D621 | 14.0 | % | ||
| 磨损因数 | ASTM D3702 | 60 | 10~8mm3/N·m | ||