性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
物理性能 | 比重 | ASTM D792 | 1.21 | g/cm3 | |
流动熔流率 | 230℃/2.16kg | ASTM D1238 | 17 | g/10min | |
流动收缩率 | 2.00mm | ASTM D955 | 1.2 | % | |
平衡吸水率 | 23℃,65%RH | ASTM D570 | 0.40 | % | |
硬度计硬度 | 支撑 A | JIS K6301 | 96 | ||
硬度计硬度 | 支撑 D | ASTM D2240 | 48 | ||
机械性能 | 抗张强度 | ASTM D638 | 30.0 | MPa | |
50%应变 | ASTM D638 | 10.8 | MPa | ||
断裂伸长率 | ASTM D638 | 720 | % | ||
弯曲模量 | ASTM D790 | 108 | MPa | ||
压缩强度 | 10%应变 | ASTM D695 | 10.2 | MPa | |
抗泰伯磨耗 | 1000 Cycles | ASTM D1044 | 15.0 | mg | |
拉伸应力 | 50%应变 | ASTM D412 | 9.80 | MPa | |
撕裂强度 | ASTM D624 | 118 | kN/m | ||
压缩永久变形 | ASTM D395 | 60 | % | ||
悬壁梁缺口冲击强度 | ASTM D256 | 无断裂 | |||
热性能 | 热变形温度 | 1.8MPa,未退火 | ASTM D648 | 68.0 | ℃ |
脆化温度 | ASTM D746 | < -65.0 | ℃ | ||
维卡软化温度 | ASTM D1525 | 172 | ℃ | ||
熔融温度 | DSC | 200 | ℃ | ||
流动线形膨胀系数 | ASTM D696 | 0.00019 | ℃ | ||
UL 阻燃等级 | UL 94 | HB | |||
电气性能 | 体积电阻率 | ASTM D257 | 2.0E+12 | ohm.cm | |
介电强度 | ASTM D149 | 25 | kV/mm |