性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
其它性能 | 比重 | ASTM D-792 | 1.22 | ||
机械性能 | 压缩调整 | 22 hours @ 70℃ | 65 | % | |
Brookfield Viscosity | 15% T.S.in THF | RVT Spindle #2,20 RPM,23℃ | 600 | cps | |
100%模量伸长率 | ASTM D-412(ASTM D-638) | 9.7 | MPa | ||
拉伸强度 | ASTM D-412(ASTM D-638) | 50.3 | MPa | ||
断裂强度 | ASTM D-624,Die C | 92.8 | KN/m | ||
Taber Abrasion | CS-17 wheel,1000g load | ASTM D-1044 | 2.6 | mg/1000 cycles | |
极限伸长率 | ASTM D-412(ASTM D-638) | 380 | % | ||
Split Tear Resistance | ASTM D-470 | 68.3 | KN/m | ||
洛氏硬度 | ASTM D-2240 | 90A(45D) | |||
压缩调整 | 22 hours @ 23℃ | 18 | % | ||
300%模量伸长率 | ASTM D-412(ASTM D-638) | 34.5 | MPa | ||
Adhesion to PET | Cast in THF | TP-141 | 0.04 | KN/m | |
拉伸调整 | ASTM D-412 | 17 | % | ||
热性能 | 维卡软化点 | ASTM D-1525 | 92 | ℃ | |
玻璃化转变温度 | DSC | -3 | ℃ | ||
其它性能 | Open Time | ASTM D-4497-94 | <5 | sec | |
Gradient Bar Tack Temperature | 161 | ℃ | |||
T-peel,Mylar Film | ASTM D-1876-72 | 2.3 | KN/m | ||
Ring and Ball Softening Point | ASTM E-28-92 | 187 | ℃ | ||
T-peel,Aluminum Foil | ASTM D-1876-72 | 0.4 | KN/m | ||
Melt Viscosity @ 204 C(400℃) | ASTM D-1084-88 | 85,000 | cps |