断裂伸长率 | 300% | 密度 | 1.31g/cm3 | 吸水率 | 0.08% |
弯曲模量 | 2340MPa | 缺口冲击强度 | 53.4 | 加工级别 | 注塑级 |
|
产品简述
断裂伸长率 | 300% | 密度 | 1.31g/cm3 | 吸水率 | 0.08% |
弯曲模量 | 2340MPa | 缺口冲击强度 | 53.4 | 加工级别 | 注塑级 |
详细数据
订购指南
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
物理性能 | 密度 | ASTM D792 | 1.31 | g/cm3 | ||
吸水率 | ASTM D570 | 0.08 | % | |||
机械性能 | 屈服拉伸强度 | ASTM D638 | 51.7 | Mpa | ||
断裂拉伸强度 | ASTM D638 | 51.7 | Mpa | |||
断裂伸长率 | ASTM D638 | 300 | % | |||
弯曲模量 | ASTM D790 | 2340 | Mpa | |||
屈服弯曲强度 | ASTM D790 | 82.7 | Mpa | |||
断裂弯曲强度 | ASTM D790 | 82.7 | Mpa | |||
Izod缺口冲击强度 | ASTM D256 | 53.4 | J/m | |||
Izod无缺口冲击强度 | ASTM D4812 | 1600 | J/m | |||
洛氏硬度 | ASTM D785 | 117 | R | |||
电气性能 | 体积电阻率 | ASTM D257 | >4.0E+16 | Ohm.cm | ||
介电强度 | 1.6mm | ASTM D149 | 23 | KV/mm | ||
介电常数 | 100Hz | ASTM D150 | 3.3 | |||
介电损耗 | 100Hz | ASTM D150 | 0.002 | |||
热性能 | 热变形温度 | - | 1.8Mpa | ASTM D648 | 54.4 | ℃ |
- | 0.45Mpa | ASTM D648 | 154 | ℃ | ||
阻燃性 | UL94 | HB |