| 牌号 | ATI Steel ATI 17-4™ |
| 厂家 | Allegheny Technologies Incorporated |
| 分类 | Steel |
| 介绍 | ATI 17-4™ precipitation hardening stainless steel (S17400), Type 630, is a chromium-nickel-copper precipitation hardening stainless steel used for applications requiring high strength and a moderate level of corrosion resistance. High strength is maintained to approximately 600°F (316°C). This alloy is designated Grade or Type 630 in several specifications. The S17400 alloy is martensitic in structure in the annealed condition and is further strengthened by a low temperature treatment which precipitates a copper containing phase in the alloy. In comparison to many alloys in the precipitation hardening family, the S17400 alloy requires a simple heat treatment; a one step process conducted at a temperature in the range 900°F (482°C) to 1150°F (621°C) depending on the combination of strength and toughness desired. A wide range of properties can be produced by this one step heat treatment. Heat treatment in the 900°F (482°C) range produces highest strength, although slightly less than that of alloys like S17700 or S15700. The latter precipitation hardening stainless steels generally require more steps to complete heat treatment. |
| Allegheny Technologies Incorporated 产品展示 | 种类 |
|---|---|
| ATI Steel ATI 610™ | Steel |
| ATI Steel ATI 420HC™ | Steel |
| ATI Steel ATI 403™ | Steel |
| ATI Steel ATI 13-8 (Bar & Billet) | Steel |
| ATI Steel ATI 2304™ | Steel |
| ATI Steel ATI 436S™ | Steel |
| ATI Steel ATI Staballoy AG17™ | Steel |
| ATI Steel ATI 800™ | Steel |
| ATI Steel ATI 409HP™ (UNS S40930) | Steel |
| ATI Steel ATI 309S™ | Steel |
订购说明